Specification :

1. Characteristics:
l One component, RTV-1, Neutral Curing at room temperature, high strength silicone structural sealant;
l Excellent weatherproofing performance, shelf life reaches over 30 years in general weather condition;
l No need to prime coated, excellent joint to most building material;
l Excellent compatibility with other neutral silicone sealant
2. Main Purpose:
l Structural assembling for glass curtain-wall engineering;
l Can joint glass with metal part to a single assemble part to satisfy with design of full-hided or semi-exposed flame curtain wall;
l Secondary seal and joint structural insulating glass;
l Seal in the situation of high sealed security;
3. Main Technology Data:
Performance Standard Measured Value Testing Method
Slumpability Horizontal Not change shape Not change shape GB/T 13477
Vertical(mm) d3 0 GB/T 13477
Pot Life when 20min,S d10 3.3 GB/T 13477
Skin Time(h) d3 1.2 GB/T 16776
Hardness(HsA) 20-60 43 GB/T 531
Thermogravimetry(%) d10 4.2 GB 16776
Tentile Proper(MPA) in standard condition e0.60 0.99 GB/T 13477
Tentile Proper(MPA) at 90 e0.45 0.87 GB/T 13477
Tentile Proper(MPA) at -30 e0.45 1.65 GB/T 13477
Tentile Proper(MPA) after flooding e0.45 0.99 GB/T 13477
Tentile Proper(MPA) after flooding and UVA irradiation e0.45 1.05 GB/T 13477
Tentile Proper(MPA) AT 23 Tensile Strength in Adhesion (%) e100 187 GB/T 13477
Storage 9 months shelf life if stored below 27 in cool, dry places after the date of production

4. Application Standard:
GB 16776-2005
5. Specification
l 300ml/cartridge; 24cartridge/ctn
l 590ml/sausage; 20sausage/ctn
l Color: black, others of special order
6. Restriction of Usage:
Not compatible with materials with grease or exudation;
Unsuitable for the airproof location, because it is required to absorb moisture in air to cure;
Unsuitable for the frosty or moist surface;
Unsuitable for the continually flooding or entire-year moist places;
Cannot be used on the unclean or unstable substrate;
Cannot be used on the substrate surface under 6 or above 40
Cannot be used on joint bearing structural strength or places of physical damage.