Product name Homopolymer Polypropylene( PP) Resins
Type HP 5400
Iteam Standard Result
Haze 40 % ( 1 mm) 40 % ( 1 mm)
Density 0.9 g/ cm³ 0.9 g/ cm³
Melt flow rate ( MFR) 3.2 g/ 10 min ( 230° C/ 2.16Kg) 3.2 g/ 10 min ( 230° C/ 2.16Kg)
Melt volume flow rate 4.3 cm³ / 10min ( 230° C/ 2.16Kg) 4.3 cm³ / 10min ( 230° C/ 2.16Kg)
Nucleator 2% -3% 2%
Tensile Modulus 1600 MPa 1600 MPa
Tensile Stress at Yield 37 MPa 37 MPa
Tensile Strain at Break > 50 % 60 %
Tensile Strain at Yield 9 % 9 %
Charpy unnotched impact strength 190 kJ/ m² ( 23 ° C) 190 kJ/ m² ( 23 ° C)
Charpy notched impact strength 4 kJ/ m² ( 23 ° C) 4 kJ/ m² ( 23 ° C)
Vicat softening temperature 154 ° C ( A50 ( 50° C/ h 10N) ) 154 ° C ( A50 ( 50° C/ h 10N) )
Ball indentation hardness 78 MPa
( H 358/ 30) 78 MPa
( H 358/ 30)
Gloss 113 % ( 60° ) 113 % ( 60° )