HDPE-High Density Polyethylene

Quantity Order:

Origin:

China

Payment Method:

Telegraphic Transfer (T/T)

Properties Test Method Unit 2200J
Melt Flow Rate ( MFR) 190 o C ASTM D-1238 g/ 10min 5.0
Mold Shrinkage HPC Method % 1.8
Density2 ASTM D-1505 g/ cm3 0.965
Softening Point ASTM D-1525 o C 124
Tensile Strength at Yield ASTM D-638 Kg/ cm² 260
Ultimate Elongation ASTM D-638 % 300min
Heat Distortion
Temperature( 4.6cm/ cm² ) ASTM D-648 o C 78
Flexural Modulus of Elasticity ASTM D-790 Kg/ cm² 14000
Hardness( Rockwell) ASTM D-785 R 68
Du-Pont Impact Strength
( 23 o C) HPC Method 100
IZOD Impact Strength ( 23 o C) ASTM D-256 Kg* cm/ cm 10
ESCR ASTM D-1693 F 50HR 5